Products
- Organic Salt[6]
- Organic Acid[6]
- Nitrogen Fertilizer[6]
- Alcohol & Hydroxybenzene & Ether[6]
- Chemical Auxiliary Agent[6]
- Organic Intermediate[2]
- Sulphate[6]
- Flavour & Fragrance[6]
- Oxide[3]
- Inorganic Acids[4]
- Ester & Derivatives[6]
- Silicate[5]
- Palm Oil[4]
- Other Chemicals[3]
- Carbonate[2]
- Polymer[6]
- Other Inorganic Salts[3]
- Other Plant & Animal Oil[3]
- Biodiesel[1]
- Food Additives[6]
- Compound Fertilizer[1]
- Concrete Admixtures & Mortar Admixtures[1]
- Zinc Ingots[5]
- Water Treatment[6]
- Phosphate[1]
- Daily Chemicals[6]
- Pigment[6]
- Paint & Coating[1]
- Paraffin[6]
- Bitumen[1]
- Lubricant[1]
- Aluminum Ingots[6]
- Tin Ingots[2]
- Lead Ingots[1]
- Magnesium Ingots[1]
- Halide ( Except Chloride )[2]
- Vaseline[2]
- Other Fertilizers[4]
- Feed Additives[1]
- HDPE[6]
- LDPE[2]
- PET[1]
- PP[6]
- HIPS[1]
- PS[3]
- ABS[2]
- EPS[1]
- Other Household Chemicals[1]
- Soap[2]
- Detergent[4]
- Nitrate[3]
- Other Rubber Products[1]
- Plant Extract[1]
- LLDPE[1]
- PVC[1]
- Pet Apparel & Accessories[1]
- EVA[1]
Contact Us
- Contact Person : Mr. Xu Jack
- Company Name : Hebei Eminent Chemical Technology Co., Ltd.
- Tel : 86-311-80872088
- Fax : 86-311-80872099
- Address : Hebei,Shijiazhuang,No.50 Zhaiying Street, Shijiazhuang City, Hebei
- Country/Region : China
High quality GPPS Resin
Product Detailed
Related Categories:PS
Related Product Searches:High quality GPPS Resin,High Quality,polystyrene gpps hips, gpps polystyrene
1.Competitive price
2, Good colorability and electrical properties
3.UL SGS CSA ROSH
4.certificate: ISO9001:2
Related Product Searches:High quality GPPS Resin,High Quality,polystyrene gpps hips, gpps polystyrene
HOT
Specification: Injection moulding, extrusion, medical usage Uasge: CD box, drink cup, egg box, extrusion package materials, medical articles, vegetable box in refrigerator
| Item | Test conditions | Test method | Test data | unit |
| Density | ISO 1183:1987 | 1040 | kg/m3 | |
| Water absorption | ISO 62:1999 | <0.1 | % | |
| Melt flow rate | 200°C/5kg | ISO 1133:1997 | 3.8 | cm3/10min |
| Process shrinkage | ISO 294-4:1997 | 0.4-0.6 | % | |
| Charpy impact strength | 1eU | ISO 179:1993 | 15 | kj/m2 |
| Tensile modulus | 1mm/min | ISO 527-2:1993 | 3300 | MPa |
| Elongation | 50mm/min | ISO 527-2:1993 | 3 | % |
| Tensile strength at break | 50mm/min | ISO 527-2:1993 | 55 | MPa |
| Ball indentation hardness H | 358N/30s | ISO 2039-1:1993 | 150 | N/mm2 |
| Bending strength | 2mm/min | ISO 178:1993 | 100 | MPa |
| HDT | 1.8MPa | ISO 75-2:1993 | 84 | °C |
| Linear coefficient of thermal expansion | (23-80)°C | DIN 53 752 | 0.8-1.0 | K-1 |
| Heat conduction | DIN 52 612 | 0.16 | W/mK | |
| Vicat softening point | B50/oil | ISO 306:1994 | 93 | °C |
| Flame retardance | >1.4mm | UL-Standard 94 | 94HB | Class |
High quality GPPS Resin